Characteristics of amorphous alloy catalyst - activation


The amorphous alloy powder was added to the aqueous solution of sodium hydroxide containing additives for activation treatment and washed with water.
  
The activation reaction formula is:
2NiAl+2NaOH+2H2O = 2NaAlO2+3H2+2Ni
  
The activation specific surface area is 140m2/g, which is much higher than that of Raini nickel, and the amorphous structure significantly improves the activity, stability and service life of the catalyst.


 

Related news


Reni nickel catalyst science knowledge(1)

Physical and chemical properties: Reni nickel catalyst before activation is silver-gray amorphous powder (nickel-aluminum alloy powder), with a moderate degree of flammability, partial activation in the presence of water and the production of hydrogen easy agglomeration, long-term exposure to air is easy to weather. Nickel-aluminum alloy powder is activated into gray-black particles, accompanied by active hydrogen, extremely unstable, oxidative combustion in the air, must be immersed in water or ethanol for preservation. It was first used by American engineer Murray Rainey as a catalyst in the hydrogenation of vegetable oils. The preparation process is to treat nickel-aluminum alloy with concentrated sodium hydroxide solution, in this process, most of the aluminum will react with sodium hydroxide and dissolve, leaving a lot of micropores of different sizes. In this way, the surface of Raininickel is a fine gray powder, but from a microscopic point of view, each tiny particle in the powder is a three-dimensional porous structure, this porous structure greatly increases its surface area, and the large surface area brings high catalytic activity, which makes Raininickel widely used as a heterogeneous catalyst in organic synthesis and industrial hydrogenation reactions. Since "Rainey" is a registered trademark of Grace Chemicals, strictly speaking, only products manufactured by the company's Davidson Chemical Division can be called "Lanny Nickel". The term "metal backbone catalyst" or "sponge-metal catalyst" is used to refer to catalysts with a microporous structure and physical and chemical properties similar to Raney nickel.